extrudeuse à vis cylindrique/conique à double vis conception pour wpc Spécification 45/90, 45/100, 50/105, 51/105, 55/110, 55/120, 58/124, 60/125, 65/120, 65/ 132, 68/143, 70/135, 70/140, 75/150, 80/143, 80/156, 92/188 Ce qui précède sont des spécifications standard, nous pouvons personnaliser selon les exigences des clients.
| Product | Bimetallic twin conical screw and barrel |
| Hardness after hardening and tempering | HB260°~320° |
| Nitrided Hardness | HV950°~1000° |
| Nitrided Depth | 0.50~0.7mm |
| Nitrided Brittleness | above 2 stage |
| Surface Roughness | Ra0.4 |
| Screw straightness | 0.015mm |
| Hardess of surface chromium-plating after Nitriding | HV≥950HV |
| Chromium-plating Depth | 0.05~0.10mm |
| ALLoy Depth | 0.8~2.0mm |
| Alloy hardness | HRC56°~65° |
| Alloy | iron,nickel,tungsten,molybdenum |
| Types of screw | Gradual type,mutant type,wave type,barrier type,double screen type,shunt type,separation type,exhaust type,pin type,mixed type,double-head type,three-head type,multi head type etc. |
Base Materials: | 1)38CrMoAlA(SACM 645) 2)42CrMo(AISI 4140) 3)Cr12MoV(SKD11) 4)4Cr5MoSiV1(SKD61) 5)9Cr18MoV 6)40Cr |
Bimetallic Alloy Materials: | 1)Fe-based alloy 2)Ni-based alloy 3)Co-based alloy 4)Tungsten carbide |
Processing Technology: | Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting |
nous pourrions fabriquer toutes sortes de vis et de barils selon l'exigence du client. Notre vis et notre baril peuvent assurer des performances élevées et une faible consommation d'énergie pour la machine d'extrusion.
De plus, nous pouvons fournir les conceptions les plus optimales de baril à vis avec vos besoins.